提升类金刚石(Diamond-Like Carbon, DLC)膜在被保护基底上的附着能力具有明显的实际应用价值。从微观机理上分析了前期设计的Cu基多层DLC膜有效性的原因。在此基础上,研究了DLC/SiC循环层中两者厚度比例对膜层的附着性能、纳米硬度和耐磨性的影响,以优化结构、进一步提升实际应用所需的膜层性能。纳米划痕和压痕测试结果表明:随着DLC层与SiC层厚度比例的增大,多层DLC膜在Cu基上附着性能逐渐降低,但当厚度比小于2.3时,仍接近厚度400 nm的单层DLC膜在Si基上的附着性能；Cu基多层DLC膜的纳米硬度逐渐提高,同时,耐磨性接近纯DLC膜。     

制导导弹试验仿真中的目标模拟技术

介绍了制导导弹试验仿真中采用的典型目标模拟技术和目前的发展状况,这些目标模拟技术主要包括:信号直接注入技术和目标影像投影技术。详细介绍了几种目标模拟技术的优缺点以及未来的发展趋向。     

吸湿环境对石英纤维增强环氧树脂面板/PMI泡沫夹层结构复合材料吸湿行为的影响

研究了不同温度、湿度环境下,夹层结构石英纤维增强环氧树脂面板/PMI泡沫夹层结构复合材料及其芯材和面板的吸湿规律。将石英纤维增强环氧树脂面板、PMI泡沫、复合材料面板/PMI泡沫夹层结构试样在不同吸湿环境中进行吸湿处理后,对其吸湿行为进行分析。结果表明:浸水环境下面板、PMI泡沫、PMI泡沫夹层结构复合材料都表现出更为严重的吸湿行为;在潮湿环境中,50℃至70℃范围内,温度越高,试样在吸湿过程中的质量损失越多,最终的饱和吸湿率越小;在60℃以内的潮湿环境中,PMI泡沫夹层结构复合材料的饱和吸湿率可以通过相同环境下面板复合材料和PMI泡沫的吸湿率进行预测。     

Effect of tool rotational speed on the particle distribution in friction stir welding of AA6092/17.5 SiCp-T6 composite plates and its consequences on the mechanical property of the joint

This study investigates the effect of tool rotational speed (TRS) on particle distribution in nugget zone (NZ) through quantitative approach and its consequences on the mechanical property of friction stir welded joints of AA6092/17.5 SiC_p-T6 composite. 6 mm thick plates are welded at a constant tool tilt angle of 2° and tool traverse speed of 1 mm/s by varying the TRS at 1000 rpm, 1500 rpm and 2000 rpm with a taper pin profiled tool. Microstructure analysis shows large quantity of uniformly shaped smaller size SiC particle with lower average particle area which are homogeneously distributed in the NZ. The fragmentation of bigger size particles has been observed because of abrading action of the hard tool and resulting shearing effect and severe stress generation due to the rotation of tool. The particles occupy maximum area in the matrix compared to that of the base material (BM) due to the redistribution of broken particles as an effect of TRS. The migration of particles towards the TMAZ-NZ transition zone has been also encountered at higher TRS (2000 rpm). The microhardness analysis depicts variation in average hardness from top to bottom of the NZ, minimum for 1500 rpm and maximum for 2000 rpm. The impact strength at 1000 rpm and 1500 rpm remains close to that of BM (21.6 J) while 2000 rpm shows the accountable reduction. The maximum joint efficiency has been achieved at 1500 rpm (84%) and minimum at 1000 rpm (68%) under tensile loading. Fractographic analysis shows mixed mode of failure for BM, 1000 rpm and 1500 rpm, whereas 2000 rpm shows the brittle mode of failure.     

Effects of jute fibre content on the mechanical and dynamic mechanical properties of the composites in structural applications

Due to notable characteristics, sustainability concept and environmental issues, hybridisation natural with synthetic fibres to fabricate composites have been rapidly gaining market share in different applications (structural, military, aerospace and automotive vehicles). Compression, tension and fatigue tests of various stacking sequences of plain jute/carbon reinforced (PVB) polyvinyl butyral by hot hydraulic press technique were experimentally conducted. Six types of fabricated composites with various constituents (jute, carbon and their hybrids) were fabricated and tested. Notably, fatigue lifetime of hybrids increases with increasing the carbon content relative to the jute fibre content. On the other hand, Jute composites possess high strain compared to pure carbon composite, which gives an overall improvement in mechanical behaviours. Interestingly, H1 hybrid with Carbon/Jute/Carbon sequences offers similar fatigue stiffness behaviour of H3 hybrid with Carbon/Jute/Carbon/Jute sequences when subjected to cyclic loading. Carbon composite (C) exhibited the highest fatigue resistance, whiles jute composite (J) possessed the highest strain and semi brittle trends in both mechanical and fatigue performance. Results concluded that plain jute fibres could partially replace high-cost synthetic carbon fibres to produce more eco-friendly hybrids to be utilised in different composites industries.     

断裂复合材料层压板贴片快速修复工艺研究

采用CMR-1A复合材料热补仪和3234/G814复合材料预浸料贴片,对完全断裂的复合材料层压板进行双面修复。通过正交试验法获得了最佳修复工艺参数:固化温度为130℃;固化时间为80 min;贴片层数为5层(单面);真空度为0.04 MPa;贴片长度为50 mm。对优化工艺参数进行试验验证,结果表明:复合材料层压板拉伸强度从0 MPa增加到320.84 MPa,提高了57.29%;LY12CZ铝合金和45钢板拉伸强度恢复率分别为96%和75.53%。     

FeAlCrNbB金属间化合物复合涂层的制备与表征

研究开发了一种FeAlCrNbB新型喷涂粉芯丝材,并结合自动化高速电弧喷涂工艺制备了该材料的复合涂层,分析了涂层的常规力学性能、组织结构和油润滑条件下的滑动摩擦磨损性能,并和常规FeAl涂层进行了对比。结果显示:FeAlCrNbB涂层具有相对较高的显微硬度和拉伸结合强度、低的孔隙率,组织致密,形成了由Fe-Al金属间化合物相、氧化物以及少量非晶和纳米晶组成的复合结构,由于这种复合结构的材料特征,使涂层具备较好的耐磨损性能。     

纤维缠绕复合材料管道等径三通的强度分析

根据复合材料强度准则中应用最广的Tsai—wu失效准则，利用ANSYS有限元分析软件，对纤维缠绕复合材料管道等径三通强度进行分析。分析结果表明，复合材料管道三通在承受内压时，在主管和支管的连接处会产生应力集中，纤维的缠绕方向不同三通的强度因子会各异，缠绕角在50°～60°时复合材料管道三通的强度最好，此结论可以为纤维缠绕复合材料管道三通的设计制造提供一种有效的参考。